Welcome to Maduka Metals, your trusted partner for industrial supplies right here in Abuja. We are proud to specialize in providing top-tier High Speed Steel T1 Bars, sourced to meet the rigorous demands of Nigeria’s growing manufacturing and engineering sectors. Our commitment is to deliver not just a product, but a reliable solution that empowers local workshops and large-scale industries alike, ensuring your projects are built on a foundation of quality and durability.
The composition of these T1 bars is what sets them apart, being a tungsten-based high-speed steel known for its remarkable red-hardness. This means it retains its strength and cutting edge even when exposed to the high temperatures generated during fast machining operations. This ability to withstand heat, combined with excellent wear resistance, makes it a superior choice for creating tools that need to perform under demanding conditions without losing their effectiveness.
| ASTM A600 | C | Mn | P | S | Si | Cr | V | Mo | W | Co | ||||||||
| T1 | 0.62 | 0.80 | 0.10 | 0.40 | 0.03 | 0.03 | 0.20 | 0.40 | 3.75 | 4.50 | 0.90 | 1.30 | … | … | 17.25 | 18.75 | … | … |
| DIN ISO 4957 | C | Mn | P | S | Si | Cr | V | Mo | W | Co | ||||||||
| HS18-0-1/1.3355 | 0.73 | 0.85 | … | … | … | … | … | 0.65 | 3.60 | 4.50 | 1.00 | 1.20 | … | … | 17.20 | 18.70 | … | … |
| JIS G4403 | C | Mn | P | S | Si | Cr | V | Mo | W | Co | ||||||||
| SKH2 | 0.73 | 0.83 | … | 0.40 | 0.03 | 0.03 | … | 0.45 | 3.80 | 4.50 | 1.00 | 1.20 | … | … | 17.20 | 18.70 | … | … |
| Properties | Metric | Imperial |
| Density | 8.67 g/cm3 | 0.313 lb/in3 |
| Hardness, Rockwell C | 63.0 – 65.0 | 63.0 – 65.0 |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elastic modulus | 190-210 GPa | 27557-30457 ksi |
| Country | USA | German | Japan |
| Standard | ASTM A600 | DIN EN ISO 4957 | JIS G4403 |
| Grades | T1 | HS18-0-1/1.3355 | SKH2 |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Thermal expansion | 9.7 x 10-6/ºC | 20-200 more | – |
| Thermal conductivity | 19.9 x W/m-K | 100 more | – |
Yes, High-Speed Steel T1 bars can be welded, but it requires specialized techniques like preheating and post-weld heat treatment to prevent cracking and maintain their hardness and strength properties.
High-Speed Steel T1 bars resist corrosion due to the presence of chromium, which forms a protective oxide layer on the surface. This enhances their resistance to moisture and chemical wear, prolonging tool life.
This unique combination of properties makes High Speed Steel T1 Bars incredibly versatile. They are the ideal material for crafting a wide range of cutting tools, including drill bits, taps, milling cutters, and saw blades. Beyond that, their durability makes them perfect for use in forming tools, punches, and dies, especially in operations involving high speeds where other materials would quickly soften and fail, ensuring greater efficiency and longer tool life in your workshop.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.